dc.descriptionEl presente trabajo de investigación consiste en trabajar con distintos hormigones convencionales y remplazar los materiales de agregado fino y agua por cantidades similares de resina poliéster líquida. Entonces, se espera que con estos nuevos hormigones poliméricos la resistencia a la flexión se incremente. Para poder establecer las dosificaciones del hormigón convencional se utilizó el método del A.C.I, adicionalmente se corroboró con ensayos de laboratorio para cada uno de los materiales pétreos, los ensayos realizados fueron: ensayo de granulometría, densidad aparente, compactada y suelta, densidad real, capacidad de absorción, densidad real del cemento y el ensayo de asentamiento del hormigón. Con las probetas se realizó el ensayo a compresión a los 7, 14 y 21 días de curado obteniendo así las resistencias de 210, 240 y 280 kilogramos sobre centímetro cuadrado. Además, la resina ayuda al hormigón convencional a mejorar sus propiedades químicas y mecánicas, formando así el hormigón polimérico. Después con el nuevo hormigón obtenido se procedió a realizar el ensayo de resistencia a la flexión con carga aplicada a los tercios de la luz en cada una de las vigas elaboradas. Finalmente se realizó mediante el método de Mander y Park el cálculo del diagrama Momento-Curvatura de cada viga tanto de hormigón normal como del polimérico, para realizar un análisis de cada una de las curvas obtenidas y establecer que existe un aumento en la resistencia a la flexión cuando se trabaja con resina pues el módulo de ruptura es mayor en comparación al de los otros especímenes.es_ES
dc.description.abstractThe present research work consists of working with different conventional concretes and replacing the fine aggregate materials and water with similar amounts of liquid polyester resin. Then, it is expected that with these new polymer concretes the flexural strength will increase. In order to establish the dosages of conventional concrete, the A.C.I. method was used, additionally it was corroborated with laboratory tests for each of the stony materials, the tests carried out were: granulometry test, apparent density, compacted and loose, real density, capacity absorption, real density of the cement and the concrete slump test. With the specimens the compression test was carried out at 7, 14 and 21 days after curing, thus obtaining the strengths of 210, 240 and 280 kilograms per square centimeter. In addition, the resin helps conventional concrete to improve its chemical and mechanical properties, thus forming polymeric concrete. After that, with the new concrete obtained, the flexural strength test was carried out with a load applied to thirds of the span in each of the manufactured beams. Finally, using the Mander and Park method, the calculation of the MomentCurvature diagram of each beam of both normal and polymeric concrete was carried out, to perform an analysis of each of the curves obtained and establish that there is an increase in resistance to the flexion when working with resin since the modulus of rupture is higher compared to that of the other specimens.es_ES
dc.language.isospaes_ES
dc.publisherUniversidad Técnica de Ambato. Facultad de Ingeniería Civil y Mecánica, Carrera de Ingeniería Civiles_ES
dc.rightsopenAccesses_ES
dc.subjectVIGAS CONVENCIONALESes_ES
dc.subjectVIGAS REFORZADASes_ES
dc.subjectRESINA POLIESTER LÍQUIDAes_ES
dc.subjectAGREGADO FINOes_ES
dc.subjectAGREGADO GRUESOes_ES
dc.subjectHORMIGÓN TRADICIONALes_ES
dc.subjectGRANULOMETRÍAes_ES
dc.subjectRESISTENCIA A LA COMPRESIÓNes_ES
dc.titleEstudio comparativo de la resistencia a flexión de vigas convencionales con vigas reforzadas con resina poliester liquidaes_ES
dc.typebachelorThesises_ES
Aparece en las colecciones: Ingeniería Civil

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Tesis I. C. 1417 - Chugchilan Chimborazo Nelson Hermógenes.pdfTESIS A TEXTO COMPLETO3,21 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.